Category
類 別
|
Trade
mark
牌 號
|
Chemical composition
主要成份(%)
|
Characteristics & application
特性和用途
|
Equivalent to AWS
相當(dāng)AWS
|
|
Hardfacing
硬
面
堆
焊
|
S 101
|
C3 Cr28 Ni4
Si3.5 Fe Rem.
|
HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump.
HRc48-54，耐磨、耐氣蝕、抗氧化。堆焊鏟斗齒，泵套
|
|
S 111
|
C1 Cr29 W5
Co Rem.
|
HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve.
HRc38-47，高溫下耐磨、耐蝕。堆焊高溫高壓閥門
|
ECoCr-A
|
S 112
|
C1.5 Cr29 W8
Co Rem.
|
HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass.
HRc45-50，高溫下耐磨、耐蝕。堆焊閥門，熱軋孔型
|
ECoCr-B
|
S 113
|
C2.5 Cr30 W17
Co Rem.
|
HRc≥55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage.
HRc≥55，高溫下耐磨、耐熱，但抗沖擊性差。堆焊螺旋送料機用
|
|
S 114
|
C2.5 Cr30 W12
Co Rem.
|
HRc≥53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit.
HRc≥53，高溫下耐磨、耐熱，但抗沖擊較差。堆焊牙輪鉆頭
|
ECoCr-C
|
|
Copper
alloys
銅
合
金
|
S 201
|
Sn1 Si0.3Mn0.3
Cu Rem.
|
Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper.
機械性能好，抗裂性好。紫銅氣焊及氬弧焊用
|
ERCu
|
S 211
|
Si3 Mn1
Cu Rem.
|
Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel.
機械性能好，銅合金氬弧焊及鋼的MIG釬焊用
|
ERCuSi-Al
|
S 212
|
Sn5 Cu Rem.
|
Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨性好。銅合金氬弧焊及鋼的堆焊用
|
ERCuSn-A
|
S 213
|
Sn8 Cu Rem.
|
Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨性好。銅合金氬弧焊及鋼的堆焊用
|
ERCuSn-C
|
S 214
|
Al7.5 Cu Rem.
|
Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用
|
ERCuAl-A1
|
S 215
|
Al9 Cu Rem.
|
Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用
|
ERCuAl-A2
|
S 221
|
Cu60 Sn1 Si0.3
Zn Rem.
|
Melting point is about 890℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點約890℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵
|
|
S 221F
|
Cu60 Sn1 Si 0.3
Zn Rem.
|
S221 welding rod coated with flux.
外涂焊劑的S221焊絲
|
|
S 222
|
Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.
|
Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點約880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵
|
RBCuZn-C
|
S 222F
|
Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.
|
S222 welding rod coated with flux.
外涂焊劑的S222焊絲
|
RBCuZn-C
|
S 223
|
Cu59 Sn0.6
Zn Rem.
|
Melting point is about 900℃. Braze welding of copper, steel and cast iron.
熔點約900℃。銅、鋼、鑄鐵釬焊用
|
RBCuZn-A
|
S 224
|
Cu62 Si0.5
Zn Rem.
|
Melting point is about 905℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點約905℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵
|
|
Copper
alloys
銅
合
金
|
S 225
|
Cu48 Ni10
Zn Rem.
|
Melting point is about 935℃ and high strength. Braze welding of steel, nickel and carbide alloys.
熔點約935℃。高強度,釬焊鋼、鎳及硬質(zhì)合金用
|
RBCuZn-D
|
S 225F
|
Cu48 Ni10
Zn Rem.
|
S225 welding rod coated with flux.
外涂焊劑的S225焊絲
|
RBCuZn-D
|
S 226
|
Cu60 Sn0.3
Si0.2 Zn Rem.
|
Melting point is about 900℃. Gas welding of brass, also braze welding of copper, steel and cast iron.
熔點約900℃。黃銅氣焊用，也可釬焊銅、鋼、鑄鐵
|
|
S 227
|
Cu58Sn0.9Ni0.5
Si0.1 Fe0.8
Zn Rem.
|
Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵
|
RBCuZn-B
|
S 229
|
Cu55 Ni6 Mn4
Zn余
|
Melting point is about 920℃, high strength. Braze welding of steel, nickel and hard carbide.
熔點約920℃。高強度,釬焊鋼、鎳及硬質(zhì)合金用
|
|
Aluminum alloys
鋁
合
金
|
S 301
|
Al≥99.5
|
Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum.
塑性好、耐蝕。純鋁氣焊、氬弧焊用
|
ER1100
|
S 311
|
Si5 Al Rem.
|
Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys.
抗裂性好，通用性大。鋁合金氣焊、氬弧焊用。不宜用高鎂合金
|
ER4043
|
S 321
|
Mn1.3 Al Rem.
|
Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys.
良好的耐蝕性、可焊性及塑性。鋁合金氣焊、氬弧焊用
|
|
S 331
|
Mg5 Mn0.4
Al Rem.
|
Corrosion resistance and high strength. Argon arc welding of aluminum alloys.
耐蝕，強度高。鋁合金氬弧焊用
|
ER5183
|
<